Скачать с ютуб Creating Fused Glass Flower Elements в хорошем качестве

Creating Fused Glass Flower Elements

**UPDATE 23-MAY-21** For those who use Bullseye or 90 COE, another wonderful glass artist named Caren Ashford has graciously shared the flattening schedule that worked great for her after some trial and error. Here you go. Thank you Caren! Caren Ashford’s schedule for flattening BE/90 600-1250-45, 9999-1570-1hour 20 mins 999-900-30 In this three-part video I am sharing how to make "enhanced" dots to then flatten into flower elements you can use in many fusing projects. I am using 96 COE but you can use this process with any fusible glass, just make sure whatever you mix together is compatible, testing if necessary. Depending on the glass you use, your kiln, etc. you may need to adjust the firing schedules provided. Always view any posted schedule (from anyone!) as a starting point. See my video on making test tiles to help you learn your kiln and where you should target your temperatures and holds. As always, thank you for watching!